| Customization: | Available |
|---|---|
| Feature: | Long Time Materials |
| Refractoriness (℃): | 1580< Refractoriness< 1770 |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Gongtao company mainly produce alumina tubes, rods and various industrial ceramic parts, which are mainly used in thermalcouple temperature, liquid steel continous temperature, various industrial furnace(containig vacuum furnace, carburizing furnace, wire furnace, atmosphere furnace etc), especially widely used in petrochemical, spinning, electric, instrumentation, mechanical workout, military project etc industry.
| Dimension | Outer dia. mm | Inner dia.mm | Length mm | Remark | |
| Item | |||||
| Thermocouple protection tube | 7-120 | 1-110 | 10-2000 | If you need others,we can customize for you. |
|
| Insulated tube | Single hole | 2-120 | 1-110 | 10-2000 | |
| (inner core) | Double holes | 1-10 | 0.4-2 | 10-2000 | |
| Four holes | 2-10 | 0.5-2 | 10-2000 | ||
| Material | 85 Al2o3 | 90 Al2o3 | 95 Al2o3 | 99 Al2o3 |
| Al2o3 | 85% | 90% | 93% | 99.30% |
| Fe2o3 | ≤ 1.0 | ≤ 0.5 | ≤ 0.5 | ≤ 0.3 |
| Desnsity: g / cm3 | 3.4 | 3.5 | 3.6 | 3.85 |
| Vickers Hardness | ≥ 8.6 | ≥ 8.8 | 9 | 9 |
| Water Absorption:% | ≤ 0.2 | ≤ 0.1 | ≤ 0.085 | ≤ 0.01 |
| Refractoriness:°C | 1580 °C | 1600 °C | 1650 °C | 1800°C |
| Flexural Strength:Mpa | 180 | 200 | 240 | 280 |
Wear Rate( at room temperature, erosion, 100 grinding)% |
≤ 3 | ≤ 2.5 | ≤ 1 | ≤ 0.5 |
| Feature | Application | Main usage |
| 1.Great mechanical strength | Electric appliance industry Automotive industry |
1.Heat treatment furnace and toughened furnace |
| 2.High softening temperature | ||
| 3.Good resistance to thermal impact | ||
| 4.Small thermal expansion coefficient | Mechanical industry Engineer industry |
2.Inner liner tube and heating tube in electric furnace |
| 5.Good chill and abrupt heat properties | ||
| 6. Resistance to acid and alkali corrosion |